Brazing Filler Metal
HARRIS 0620F1 SILVER PHOSCOPPER BRAZING ROD WIRE SIZE .050 X 1/8" 28 STICKS PER TUBE
- Applicable Materials: Copper to Copper and Copper to brass
- Brazing Range: 1345 to 1500 deg f
- Chemical Composition: 7.1% Phosphorus, Copper Balance and 0.15% Other
- Type: #28
- Diameter: 1/8 in
- Length: 28 in
- Container Type: Stick Tube
Harris® low cost alloy for many copper to copper applications where moderate fit-up can be maintained and brazing temperature is Not critical.
- Features
- Warranty
- Standards & Approvals
| Harris® Low cost alloy suitable for most copper-to-copper or brass joints where good fit-up exists and assemblies are not subject to excessive vibration nor movement |
| This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0005 in is a frequent choice for copper brazing |
| A suitable choice for brazing brass, operators should take care to avoid over heating the brass and use Harris® Stay-Silv® white brazing flux in this application |
| Not recommended for brazing steel or other ferrous base metals, the phosphorus content will form a low ductility intermetallic with the base metal |
| Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys, including Harris®, should not be used if the braze is exposed to sulfur or sulfur compounds in service |
| 1 Year |
| AWS A5.8 BCuP-2 |
| ASME Section IIC SFA 5.8 BCuP-2 |
| ISO 17672 CuP 181 |
| PROP65: Cancer and Reproductive Harm - www.P65Warnings.ca.gov |
| RoHS Compliant |